dc.contributor.advisorGarcia, Carlos Mariopt_BR
dc.contributor.authorVichessi, Raquel Brazpt_BR
dc.contributor.otherUniversidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia e Ciência dos Materiais - PIPEpt_BR
dc.date.accessioned2021-05-07T14:56:05Z
dc.date.available2021-05-07T14:56:05Z
dc.date.issued2010pt_BR
dc.identifier.urihttps://hdl.handle.net/1884/45769
dc.descriptionOrientador: Prof. Dr. Carlos Mario Garciapt_BR
dc.descriptionDissertação (mestrado) - Universidade Federal do Paraná, Setor de Tecnologia, Programa de Pós-Graduação em Engenharia e Ciência dos Materiais - PIPE. Defesa: Curitiba, 26/05/2010pt_BR
dc.descriptionInclui referências : f. 70-74pt_BR
dc.descriptionÁrea de concentração: Engenharia e ciência de materiaispt_BR
dc.description.abstractResumo: O estudo da influência na formação de placas negativas de baterias chumbo-ácido em diferentes pHs de solução de formação e, posterior avaliação das propriedades das placas formadas foi realizado neste trabalho. A caracterização destas amostras foi realizada por distintos procedimentos, resultando nos valores de capacidade, macroporosidade, quantidade de material ativo negativo e área superficial B.E.T.. Medidas de Espectroscopia de Impedância Eletroquímica (EIS), no modo galvanostático, foram efetuadas para caracterização das placas negativas em diferentes quantidades de descarga. A partir dos diagramas de EIS, foram obtidos os parâmetros de resistências em série e resistências de polarização. A correlação entre os resultados obtidos para as diferentes formações visou um maior conhecimento da estrutura porosa da placa negativa e seu comportamento durante o processo de descarga com a formação do filme de PbSO4. Palavras-chave: baterias chumbo-ácido; placa negativa; área superficial B.E.T.; EIS.pt_BR
dc.description.abstractAbstract: The study of formation lead-acid batteries negative plates in different pHs formation solutions and subsequent evaluation of the properties of plate had been done on this work. The characterization of these samples was performed by different procedures, resulting in values of capacity, macroporosity, amount of negative active material and B.E.T. surface area. Measures of Electrochemical Impedance Spectroscopy (EIS), galvanostatic mode, were performed to characterize the negative plates in different amounts of discharge. From the EIS diagrams, the study obtained the parameters of resistance in series and polarization resistances. The correlation between the results obtained for the different formation solutions was a better understanding of the porous structure of the negative plate and its behavior during the discharge process with the formation of film PbSO4. Keywords: lead-acid battery; negative plate; BET superficial area; EIS.pt_BR
dc.format.extent74 f. : il. algumas color., grafs., tabs.pt_BR
dc.format.mimetypeapplication/pdfpt_BR
dc.languagePortuguêspt_BR
dc.relationDisponível em formato digitalpt_BR
dc.subjectEngenharia de Materiais e Metalurgiapt_BR
dc.subjectBaterias elétricaspt_BR
dc.subjectChumbopt_BR
dc.subjectEnergia - Armazenamentopt_BR
dc.subjectTesespt_BR
dc.titleEstudo das condições de formação de placas negativas de baterias chumbo-ácido e caracterização por espectroscopia de impedância eletroquímicapt_BR
dc.typeDissertaçãopt_BR