    Estudo das condições de formação de placas negativas de baterias chumbo-ácido e caracterização por espectroscopia de impedância eletroquímica

    Thumbnail
    View/Open
    R - D - RAQUEL BRAZ VICHESSI.pdf (2.783Mb)
    Date
    2010
    Author
    Vichessi, Raquel Braz
    Metadata
    Show full item record
    Abstract
    Resumo: O estudo da influência na formação de placas negativas de baterias chumbo-ácido em diferentes pHs de solução de formação e, posterior avaliação das propriedades das placas formadas foi realizado neste trabalho. A caracterização destas amostras foi realizada por distintos procedimentos, resultando nos valores de capacidade, macroporosidade, quantidade de material ativo negativo e área superficial B.E.T.. Medidas de Espectroscopia de Impedância Eletroquímica (EIS), no modo galvanostático, foram efetuadas para caracterização das placas negativas em diferentes quantidades de descarga. A partir dos diagramas de EIS, foram obtidos os parâmetros de resistências em série e resistências de polarização. A correlação entre os resultados obtidos para as diferentes formações visou um maior conhecimento da estrutura porosa da placa negativa e seu comportamento durante o processo de descarga com a formação do filme de PbSO4.
     
    Abstract: The study of formation lead-acid batteries negative plates in different pHs formation solutions and subsequent evaluation of the properties of plate had been done on this work. The characterization of these samples was performed by different procedures, resulting in values of capacity, macroporosity, amount of negative active material and B.E.T. surface area. Measures of Electrochemical Impedance Spectroscopy (EIS), galvanostatic mode, were performed to characterize the negative plates in different amounts of discharge. From the EIS diagrams, the study obtained the parameters of resistance in series and polarization resistances. The correlation between the results obtained for the different formation solutions was a better understanding of the porous structure of the negative plate and its behavior during the discharge process with the formation of film PbSO4.
     
    URI
    https://hdl.handle.net/1884/45769
    Collections
    • Dissertações [128]

    DSpace software copyright © 2002-2022  LYRASIS
    Contact Us | Send Feedback
    Theme by 
    Atmire NV
     

     

    Browse

    All of DSpaceCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsxmlui.ArtifactBrowser.Navigation.browse_typeThis CollectionBy Issue DateAuthorsTitlesSubjectsxmlui.ArtifactBrowser.Navigation.browse_type

    My Account

    LoginRegister

    Statistics

    View Usage Statistics

    DSpace software copyright © 2002-2022  LYRASIS
    Contact Us | Send Feedback
    Theme by 
    Atmire NV