Mostrar registro simples

dc.contributor.advisorRoman, Lucimara Stolz, 1971-pt_BR
dc.contributor.otherUniversidade Federal do Paraná. Setor de Ciências Exatas. Programa de Pós-Graduação em Físicapt_BR
dc.creatorBassi, Maiara de Jesuspt_BR
dc.date.accessioned2024-10-14T19:43:09Z
dc.date.available2024-10-14T19:43:09Z
dc.date.issued2017pt_BR
dc.identifier.urihttps://hdl.handle.net/1884/54919
dc.descriptionOrientadora: Profª. Drª. Lucimara Stolz Romanpt_BR
dc.descriptionDissertação (mestrado) - Universidade Federal do Paraná, Setor de Ciências Exatas, Programa de Pós-Graduação em Física. Defesa : Curitiba, 22/02/2017pt_BR
dc.descriptionInclui referênciaspt_BR
dc.description.abstractResumo: Neste estudo, células solares orgânicas baseadas na estrutura de heterojunção em volume, onde a camada ativa é composta por uma mistura utilizando PSiF-DBT como material doador de elétrons e PC71BM como aceitador de elétrons foram investigadas através de medidas ópticas, morfológicas e elétricas. Foram fabricados dispositivos sem tratamento térmico, e com a camada ativa tratada termicamente a 100 °C e 200 °C. Como uma forma alternativa do controle morfológico, foi utilizado o aditivo DIO em solução, onde foram fabricados dispositivos sem tratamento térmico e tratado a 100 °C. Foi observado que a eficiência de conversão de potência diminui com o efeito da temperatura para dispositivos sem a adição do DIO. Essa diminuição pode ser atribuída à redução do valor da tensão de circuito aberto (Voc) com o aumento da temperatura, podendo estar relacionada com as mudanças morfológicas dos filmes. Após o tratamento com DIO, a eficiência aumenta com o tratamento térmico. No entanto, as mudanças morfológicas através de tratamentos térmico e aditivo não foram suficientes para melhorar a performance da blenda PSiF-DBT:PC71BM, atribuindo o melhor desempenho para dispositivos sem tratamento térmico e sem DIO. Este resultado se mostrou promissor possibilitando a eliminação da utilização de diferentes tratamentos na camada ativa de células solares orgânicas, podendo eliminar processos adicionais envolvidos na fabricação dos dispositivos.pt_BR
dc.description.abstractAbstract: In this study, organic solar cells based on bulk heterojunction structure, where the active layer is composed of a mixture using PSiF-DBT as electron donor material and PC71BM as electron acceptor was investigated through optical, morphological and electrical measurements. Devices were fabricated without thermal treatment, and the active layer was thermally treated at 100 ° C and 200 ° C. As an alternative form of morphological control, the DIO additive was used into solution, where devices were fabricated without thermal treatment and annealed at 100 ° C. It was observed that the power conversion efficiency decreases with the effect of temperature for devices without addition of DIO. This decrease can be attributed to the reduced value of the open circuit voltage (Voc) with the increase in temperature, and may be related to the morphological changes of the films. After treatment with DIO, the efficiency increases with temperature. However, the morphological changes through thermal and additive treatments are not enough to improve the performance of the PSiF-DBT: PC71BM blends, assigning the best performance for without annealing treatment and without additive solvent. This result was promising allowing the elimination of the use of different treatments in the active layer of organic solar cells, and could eliminate additional processes involved in the fabrication of the devices.pt_BR
dc.format.extent1 recurso online : PDF.pt_BR
dc.format.mimetypeapplication/pdfpt_BR
dc.languagePortuguêspt_BR
dc.subjectCelulas solarespt_BR
dc.subjectFisicapt_BR
dc.subjectGeraçao de energia fotovoltaicapt_BR
dc.subjectPolímeros conjugadospt_BR
dc.titleEstudo do efeito do tratamento térmico e aditivo na camada ativa de células solares orgânicas na estrutura de heterojunção em volumept_BR
dc.typeDissertação Digitalpt_BR